 为了更好地认识加氢脱硫和催化加氢反应中的载体影响和助剂效应，在同样的催化剂制备方法及反应条件下，研究了噻吩加氢脱硫（HDS）和四氢萘催化加氢（HYD）反应．结果表明，对于无助剂的Mo和W催化剂，载体对催化活性的影响顺序为TiO2－Al2O3＞ZrO2＞Al2O3．助剂的添加改变了催化剂活性顺序．Ni助剂催化剂的活性明显高于Co助剂催化剂．ZrO2担载的添加Ni的Mo和W催化剂分别获得了最佳的HDS和HYD活性．然而，添加Pt的Mo和W催化剂其HDS和HYD活性仅是Pt与Mo（W）二者的加和，Pt与Mo（W）之间没有协同效应．先将担载的Mo和W预硫化再将助剂引入体系的催化剂制备方法可以避免Ni和Co过早硫化形成类硫化镍（或硫化钴）物相，与采用螯合物分子方法制备的催化剂间有一定的相似性．     

在涂层TiO2改性铜催化剂上甲醇脱氢制甲酸甲酯

在常压和２５０℃下，考察了涂层ＴｉＯ２改性铜催化剂上甲醇脱氢生成甲酸甲酯的活性和选择性以及催化剂的稳定性。结果表明，涂层ＴｉＯ２明显提高了铜催化剂的活性和稳定性。在所考察的铜催化剂中，以Ｃｕ／ＴｉＯ２／ＡｌＯ３的催化活性最高，甚至高于离子交换法制备的Ｃｕ（ｅｘ）／ＳｉＯ２催化剂。ＸＰＳ分析表明，Ｃｕ／ＴｉＯ２／ＡｌＯ３中存在着两种化学环境不同的ＣＵ（０），即负载在ｒ－ＡＬＯ３和ＴｉＯ２－Ａｌ２Ｏ３     

以有机镍配合物为前体制备担载镍催化剂的研究

描述了以镍单核配合物ＮｉＣｐ２和簇合物Ｎｉ３Ｃｐ３Ｎ－ｔ－Ｃ４Ｈ９为前体的ＳｉＯ２载镍催化剂的制备，通过元素分析、ＴＲＲ、ＴＰＤＥ、ＸＰＳ，ＣＯ吸附和苯加氢反应对以镍配合物和簇合物为前体制备的催化剂的性能及其制备过程了研究和表征。结果表明，镍与合物和簇合物在担载过程中同载体ＳｉＯ２表面发生了相互作用，其化学组成发生了变化，在苯加氢反应中，此催化剂的活性比以Ｎｉ（ＮＯ３）２为前体制备的催化剂高得多，     

Redox behavior of V/MgO catalyst in H2S wet oxidation at room temperature

The room temperature wet catalytic oxidation was conducted in a batch reactor with V/MgO catalyst. The XRD study of the catalyst used indicated that V/MgO could not only oxidize H2S to sulfur selectively, but also prevent the sulfidation of metal oxide effectively at the room temperature. The XPS study indicated that the H2S oxidation with V/MgO could proceed by a redox mechanism (V⁵⁺↔ V⁴⁺) and that V³⁺ formation (V⁴⁺→ V³⁺), was responsible for the deactivation of V/MgO. This revised version was published online in June 2006 with corrections to the Cover Date.     

CO2部分氧化乙烷制乙烯Pd—Cu／MoO3—SiO2催化剂的研究

用化学吸附－红外光谱、化学吸附－程序升温脱附（ＴＰＤ）和微型反应技术研究了Ｐｄ－Ｃｕ／ＭｏＯ３－ＳｉＯ２（ＭｏＳＯ）催化剂对ＣＯ２和乙烷的吸附活化和部分氧化反应性能．结果表明，乙烷以Ｃ—Ｈ键中的Ｈ吸附于ＭｏＳＯ载体表面ＭｏＯ键的端基氧上；Ｐｄ－Ｃｕ／ＭｏＳＯ催化剂对ＣＯ２有良好的化学吸附活化性能，ＣＯ２的吸附除有线式吸附态和剪式吸附态外，还有一种新的卧式吸附态；Ｐｄ－Ｃｕ／ＭｏＳＯ催化剂的晶格氧参与了化学反应．探讨了在Ｐｄ－Ｃｕ／ＭｏＳＯ催化剂上ＣＯ２的部分氧化乙烷反应机理     

Oxidation of allylic alcohols, amines, and sulfides mediated by assembled triphase catalyst of phosphotungstate and non-cross-linked amphiphilic copolymer

A novel catalyst PWAA, an assembled complex of phosphotungstic acid (H₃PW₁₂O₄₀) and a non-cross-linked copolymer of N-isopropylacrylamide with an ammonium, was developed. It is an amphiphilic, cross-linked, and supramolecular insoluble complex and showed catalytic activity on oxidation with aqueous hydrogen peroxide. PWAA, used in 2.7×10⁻⁵-2.0×10⁻³ mol equiv., catalyzed oxidation of allylic alcohols, amines, and sulfides efficiently. The turnover number (TON) of PWAA reached up to 35,000. PWAA showed a good stability in organic/aqueous media and was reused three to five times.     

PROPERTIES OF POLYMER SUPPORTED Ni-Cu BIMETALLIC CATALYSTS PREPARED BY SOLVATED METAL ATOM IMPREGNATION

D-72 resin supported nickel-copper catalysts prepared by solvated metal atom impreg-nation (SMAI) were studied by magnetic measurements and X-ray photoelectron spectro-scopy (XPS). The Ni particles on the catalysts are very highly dispersed and displaysuperparamagnetic behaviour. Ni-Cu alloy clusters were found to be formed. The sur-face compositions are different from the bulk concentrations. In contrast with the surfaceenrichment in copper generally observed on conventional Ni-Cu catalysts, the surfaces ofthese catalysts are enriched in nickel. The nickel is in both zero and valent states, whilecopper is mainly in metallic state. Catalytic data show that the formation of Ni-Cu alloyclusters has a profound effect on the catalytic activities of the catalysts in the hydrogena-tion of furfural. The activity of the Ni:Cu ratio of one bimetallic catalysts is much higherthan that of the Ni or Cu monometallic catalyst.     

Ti2(OMe)4/SiO2催化剂的制备及其合成碳酸二甲酯的反应性能

采用表面改性和离子交换法制备了SiO2负载的Ti2(OMe)4双核桥联配合物催化剂，用IR、TPD和微反技术考察了催化剂的表面构造及CO2和CH3OH在催化剂表面上的化学吸附和反应性能。结果表明：双核桥联配合物Ti2(OMe)4以Ti-O-Si键锚定在SiO2表面上；CO2在催化剂表面存在桥式和甲氧碳酸酯基两种吸附态，其中甲氧碳酸酯基吸附态是生成DMC的关键物种；CH3OH在催化剂上只有一种分子吸附态。在150℃以下，CO2和CH3OH在Ti2(OMe)4/SiO2催化剂表面上高选择地生成碳酸二甲酯。     

STUDIES ON THE PREPARATION OF ZINC-CONTAINING ACTIVATED CARBON FIBERS AND THEIR ANTIBACTERIAL ACTIVITY

1. INTRODUCTION Microbial pollution will bring about various problems in industry and other vital fields, such as causing decomposing of materials, harming people抯 health. In order to reduce these problems, new antibacterial materials have been demanded. Recently, much attention has been paid to inorganic materials including zinc oxide [1~4]. These inorganic antibacterial materials are now substituting for organic materials to avoid releasing noxious organic molecules harmful to humans;…     

MoCo/Y, MoNi/Y氮化物催化剂的结构和CH4+CO2重整反应性能

采用氨气还原法制备了NaY分子筛负载的MoCo/Y、MoNi／Y双组氮化物催化剂，用XRD和EXAFS方法征了样品的结构，并测定了其在CH4＋CO2重整反应中的活性，在氧化态时，MoCo/Y样品中主要存在CoMoO4和Co3O4两种物相，Mo的配位状态接近于CoMoO4，而Co的配位状态更接近于Co3O4，MoNi／Y样品中主要有NiMoO4和NiO两种物相，Mo的配位状态接近于MiMoO4，而Ni的配位状态可能是NiMoO4和NiO两种化合物中Ni配位状态的平均效果，Ni-Mo之间的朴素作用似乎比Co-Mo相对较强，在氮化态时，两种样品中Mo的配位状态较为相似，但即不同于MoO3，也不同于单组分γ－Mo2N.Co和Ni的配位状态都不同于各在氧化态下的状态，且都在相同的位置出现一个新强峰，这似乎表明MoCo和MoNi生成了结构相似的氮化物，在CH4＋CO2重整反应中，氮化态MoCO/Y和MoNi/Y的活性大大超过非负载单组分γ－Mo2N催化剂，其中MoNi/Y的活性相对更好一些，且活性随Ni含量增加而提高。